Compressive Strength Of Dental Ceramics

A value of 152 mpa has been quoted for the modulus of rupture of dicor glass ceramic dentsply international york pn usa adair and grossman 1984.

Compressive strength of dental ceramics.

However the tensile strength of dental porcelain is very low 20 60 mpa. This imparts brittle nature to the ceramics 23 24 25 and tend to fracture under tensile stresses. In fact the elastic modulus of enamel is about three times greater than that of dentin and depending on the study considered it can be as much as seven times higher. Fatigue of dental ceramics in a simul ated oral environmen t j dent res.

Iso 6872 dentistry ceramic materials specifies the requirements for ceramic materials used in dentistry and also defines the basic methods for flexural strength testing. Compressive strength is therefore a useful property for the comparison of dental amalgam resin composites and cements and for determining the qualities of other materials such as plaster and investments. Dental porcelain has very stable chemical properties and outstanding esthetics which are unlikely to be influenced by time. Note that the proportional limit ultimate compressive strength and elastic modulus of enamel are greater than the corresponding values for dentin.

Even the pressure strength of dental ceramics are between 350 550 mpa the draw strength value is 20 60 mpa. Ceramics materials are used in modern dentistry in a variety of different applications including fillings crowns veneers implants and dental brackets. It has similar thermal conductivity and coefficient of thermal expansion to enamel and dentine and exhibits high compressive strength. It can be identified as a sort of ceramic that is not totally transformed into glass phase.

Alumina for example has a tensile strength of 20 000 psi 1138 mpa while the compressive strength is 350 000 psi 2400 mpa. Dental ceramics possesses very good resistance to the compressive stresses however they are very poor under tensile and shear stresses 1 11 22. 35 fair hurst cw loc kwood pe ring le rd twiggs sw. 65 7 993 997 jul 1986.

Ceramic material used in dentistry is a glassy matrix that is produced via sintering and it contains leucite crystals. Typical values of compressive strength of some restorative dental materials are given in table 5 1.